- Behavior of Hydrogen Induced Cracking Originated in Centerline Segregation
- チュウシンヘンセキ ニ キイン スル スイソ ユウキ ワレ ハッセイ キョドウ
この論文をさがす
抄録
Influence of centerline segregations on hydrogen induced cracking for sour gas line pipe was investigated. As Crack Length Ratio (CLR) mainly depends on centerline segregation in the ease of well-controlled clean steel, it may discuss CLR with centerline segregations. Distribution of centerline segregation grains and P, Mn segregation ratio are represented by the experimental formulae for each casting condition. As a result, effects of casting conditions, soaking conditions and pre-reduction conditions on CLR can be estimated qualitatively, using HIC sensitivity paramenter with those formulae. Estimated CLR corresponds fairly well to measured CLR for several heats.
収録刊行物
-
- 鉄と鋼
-
鉄と鋼 85 (4), 301-306, 1999
一般社団法人 日本鉄鋼協会
- Tweet
詳細情報 詳細情報について
-
- CRID
- 1390282680160324096
-
- NII論文ID
- 110001457061
-
- NII書誌ID
- AN00151251
-
- ISSN
- 18832954
- 00211575
-
- NDL書誌ID
- 4700903
-
- データソース種別
-
- JaLC
- NDL
- Crossref
- CiNii Articles
-
- 抄録ライセンスフラグ
- 使用不可