NaOH-NaClによる固体高炭素フェロマンガン粒の脱りん

DOI Web Site Web Site

書誌事項

タイトル別名
  • Dephosphorization of Solid High-carbon Ferromanganese by NaOH-NaCl
  • NaOH-NaClによる固体高炭素フェロマンガン粒の脱りん(寄書)
  • NaOH NaCl ニヨル コタイ コウ タンソ フェロマンガンリュウ ノ ダ

この論文をさがす

抄録

Solid ferromanganese particles ranging from 0.59 to 2.38 mm in diameter were dephosphorized using NaOH-NaCl melts at temperatures of 900 to 1000°C. Thermodynamically, the oxidation of phosphorus from ferromanganese without oxidation loss of manganese is very difficult, and hence sodium hydroxide was chosen from the consideration that sodium has strong tendency to form the phosphate. The dephosphorization of 60 to 70% was attained at best with lOg of ferromanganese and 1 gNaOH-2gNaCl mixture at 950°C by 2 hours treatment. Dephosphorization did ont proceed when sodium chloride was not added to sodium hydroxide, in which case only manganese was oxidized.