- Mechanical Properties of Cold-worked and High-Low Temperature Duplex Aged Ti-15V-3Cr-3Sn-3A1 Alloy
- 冷間加工後高温-低温2段時効したTi-15V-3Cr-3Sn-3Al合金の機械的性質
- レイカン カコウゴ コウオン テイオン 2ダン ジコウシタ Ti 15V 3C
この論文をさがす
抄録
Mechanical properties were studied by tensile test of Ti-15V-3Cr-3Sn-3A1 alloy obtained by duplexaging after cold-swaging, i.e. aging at higher temperatures followed by reaging at a lower temperature. Combinations of short-time aging at 823 K, 873 K and 923 K and reaging at 673 K have improved strength-ductility balance of this alloy greatly, realizing high strength of about 1.8 GPa with tensile elongation of 5%. This duplex aging process further diminishes the influence of reduction of cold-swaging on mechanical properties after aging.
収録刊行物
-
- 鉄と鋼
-
鉄と鋼 77 (1), 131-138, 1991
一般社団法人 日本鉄鋼協会
- Tweet
詳細情報 詳細情報について
-
- CRID
- 1390282680161375616
-
- NII論文ID
- 110001481029
-
- NII書誌ID
- AN00151251
-
- ISSN
- 18832954
- 00211575
-
- NDL書誌ID
- 3694421
-
- データソース種別
-
- JaLC
- NDL
- Crossref
- CiNii Articles
-
- 抄録ライセンスフラグ
- 使用不可