Phosphorus Partition between Fe-Cr-C Melts and BaO-BaF<SUB>2</SUB> Fluxes and the Activity of BaO
-
- HARA Tohru
- Graduate School,The University of Tokyo,Now Kawasaki Steel Corp.
-
- TSUKIHASHI Fumitaka
- Faculty of Engineering,The University of Tokyo
-
- SANO Nobuo
- Faculty of Engineering,The University of Tokyo
Bibliographic Information
- Other Title
-
- 含クロム炭素飽和溶鉄とBaO-BaF<SUB>2</SUB>系フラックス間のりんの分配平衡および同系フラックス中のBaOの活量
- 含クロム炭素飽和溶鉄とBaO-BaF2系フラックス間のりんの分配平衡および同系フラックス中のBaOの活量
- ガン クロム タンソ ホウワ ヨウテツ ト BaO BaF2ケイ フラックスカ
Search this article
Abstract
The phosphorus partition between BaO-BaF2 fluxes and Fe-Cr-Csatd. alloys was measured at temperatures ranging from 1 175°C to 1 300°C under a CO atmosphere.<BR>The phosphorus partition ratio increases with increasing BaO content in the fluxes and decreases with increasing chromium content in Fe-Cr-Csatd. alloys. The BaO-BaF2 system was found to have a large phosphate capacity ranging from 1026 to 1028.5 at 1300°C, which is much larger than that for the CaO-CaF2 system. The enthalpy change for the dephosphorization reaction by BaO bearing fluxes was determined to be-528 kJ/mol. The chromium partition ratio increases with an increase in BaO content especially in the higher BaO content range. The possibility of the removal of phosphorus from Fe-16% Cr-C alloys without much oxidation loss of chromium by using 50% BaO-50% BaF2 flux was demonstrated.<BR>Furthermore, the activity of BaO for the BaO-BaF2 system was determined at 1 200°C and 1 300°C and the activity of BaF2 was calculated by using the Gibbs-Duhem relationship. The phase diagram for the BaO-BaF2 system was also discussed.
Journal
-
- Tetsu-to-Hagane
-
Tetsu-to-Hagane 76 (3), 352-359, 1990
The Iron and Steel Institute of Japan
- Tweet
Keywords
Details 詳細情報について
-
- CRID
- 1390282680161393408
-
- NII Article ID
- 110001492587
-
- NII Book ID
- AN00151251
-
- ISSN
- 18832954
- 00211575
-
- NDL BIB ID
- 3655285
-
- Data Source
-
- JaLC
- NDL
- Crossref
- CiNii Articles
-
- Abstract License Flag
- Disallowed