コバルト塩水溶液噴霧による溶融Zn-Al系合金めっき鋼板の黒変化抑制機構

DOI Web Site Web Site

書誌事項

タイトル別名
  • Inhibition Mechanism of Black Patina Development on a Hot Dip Zn-Al Alloy Coated Steel Sheet by Spraying Aqueous Solution of Co Salt
  • コバルトエン スイヨウエキ フンム ニ ヨル ヨウユウ Zn Alケイ ゴウキ

この論文をさがす

抄録

An inhibition mechanism of the black patina development on the surface of 4% Al-0.1% Mg-Zn alloy coated steel sheet by spraying aqueous solution of Co salt was investigated with various surface analytical methods.<BR>Without Co treatment, the coating surface rapidly changed its color into black in a high temperature and high humidity environment. This phenomenon was due to the formation of thick oxide film which composed of Zn, Cr and Al. The blackening of the coating surface was effectively retarded by spraying aqueous solution of Co salt onto the molten coating surface just after hot dipping.<BR>On the Co treated coating surface, a large number of Co3O4 deposits, of which structure was identified with HEED, were observed in TEM image and in IMA ion image. The thickness of this Co oxide was 0.1 0.2 μm as determined by a direct TEM observation of the ultramicrotomed cross section of the coating layer. SAM and ESCA depth-profiles showed that Co oxide retarded oxidation of the coating surface. This effect of Co oxide was attributed to cathodic inhibitive action or stable zinc hydroxide forming ability of Co ion which was eluted into the condensed water on the coating surface.

収録刊行物

  • 鉄と鋼

    鉄と鋼 76 (3), 383-390, 1990

    一般社団法人 日本鉄鋼協会

キーワード

詳細情報 詳細情報について

問題の指摘

ページトップへ