Adsorption Properties of Arsenic(V) by Polyacrylamide Cryogel Containing Iron Hydroxide Oxide Particles Prepared by <i>in situ</i> Method
-
- KUROZUMI Misa
- Department of Applied Chemistry, University of Miyazaki
-
- YANO Yasunori
- Center for International Relations, University of Miyazaki
-
- KIYOYAMA Shiro
- Department of Chemistry and Materials Technology, Miyakonojyo National College of Technology
-
- KUMAR Ashok
- Department of Biological Sciences and Bioengineering, Indian Institute of Technology Kanpur
-
- SHIOMORI Koichiro
- Department of Applied Chemistry, University of Miyazaki
Bibliographic Information
- Other Title
-
- Adsorption Properties of Arsenic(Ⅴ) by Polyacrylamide Cryogel Containing Iron Hydroxide Oxide Particles Prepared by in situ Method
Search this article
Description
Polyacrylamide (PAA) cryogels were prepared by freezing monomer solution of acrylamide with cross-linker N,N-methylenebis(acrylamide) and polymerizing initiated by N,N,Nʹ,Nʹ-tetramethyl ethylene diamine and ammonium peroxodisulfate at sub-zero temperatures. Iron hydroxide oxide particles were formed by stepwise penetration of iron(III) chloride solution (FeCl3) and alkaline aqueous solution into cryogel wall. The particles formed were observed on the surface of the cryogel wall. The amount of the particles was changed by the concentration of FeCl3 and the kind of alkaline aqueous solution. The polyacrylamide cryogel containing iron hydroxide oxide particles successfully adsorbed a large amount of As(V) at both low and high concentrations. The adsorption of As(V) with the cryogel containing iron particles was not affected by the pH value of the aqueous solution. The cryogels containing iron particles prepared using sodium carbonate had larger amount of iron than that prepared using sodium hydroxide. The adsorption amount of As(V) on the cryogel had a tendency with the contents of iron in the cryogels.
Journal
-
- Resources Processing
-
Resources Processing 62 (1), 17-23, 2015
The Resources Processing Society of Japan
- Tweet
Details 詳細情報について
-
- CRID
- 1390282680183424256
-
- NII Article ID
- 130005084012
-
- NII Book ID
- AA11907992
-
- ISSN
- 13499262
- 13486012
-
- NDL BIB ID
- 026355407
-
- Text Lang
- en
-
- Data Source
-
- JaLC
- NDL
- Crossref
- CiNii Articles
- KAKEN
-
- Abstract License Flag
- Disallowed