溶融Zn-5mass%Al合金浴におけるζ・Fe-Zn相のAl-Fe金属間化合物への変化過程

DOI Web Site Web Site 参考文献15件

書誌事項

タイトル別名
  • Changing Process from ζ·Fe-Zn Phase to Al-Fe Intermetallic Compounds in Molten Zn-5mass%Al Alloy Bath
  • ヨウユウ Zn5massパーセント Al ゴウキンヨク ニ オケル ゼータ
  • Changing Process from ζ·Fe-Zn Phase to Al-Fe Intermetallic Compounds in Molten Zn-5mass%Al Alloy Bath

この論文をさがす

抄録

As a purpose to investigate the changing process from Fe-Zn intermetallic compounds (IMCs) to Al-Fe IMCs in a molten Zn-5mass%Al alloy, this study has been carried out by immersing the galvanized steel sheet with Γ. Γ'. δ and ζ Fe-Zn phases as a coating layer in a Zn-5mass%Al bath at 450°C.<BR>ζ·Fe-Zn phase changed to particle products mainly consisted of Zn-containing Al5Fe2 and the melt with less Al concentration than the Zn-5mass%Al bath at an extremely high rate. This change was found to be occurred under the two steps reaction; (1) ζ·Fe-Zn+Al(L)→ Al-Fe-Zn amorphous phase + Zn (L), (2) Al-Fe-Zn amorphous phase →Al5Fe2 + Zn(L). At the first step, the Al-Fe-Zn amorphous phase was formed around the grain boundaries of ζ·Fe-Zn phase in contact with the Zn-5mass%Al melt and then nuclei of Al5Fe2 were formed in this amorphous phase. It is considered that Zn concentration at an area of the amorphous phase surrounded Al5Fe2 is increased with the growth of Al5Fe2. As a result, the area surrounded Al5Fe2 becomes a liquid state and Al5Fe2 changed from ζ·Fe-Zn phase exists as a particle in the Zn-rich melt. The Al-Fe-Zn amorphous phase is considered to be a quasi-equilibrium phase which has a wide range of concentration for Al (1560 at%), Fe (1025 at%) and Zn (1575 at%).

収録刊行物

  • 鉄と鋼

    鉄と鋼 84 (9), 632-636, 1998

    一般社団法人 日本鉄鋼協会

参考文献 (15)*注記

もっと見る

キーワード

詳細情報 詳細情報について

問題の指摘

ページトップへ