工業用純チタンの熱間変形抵抗と熱間加工後の再結晶挙動

DOI Web Site Web Site 参考文献12件

書誌事項

タイトル別名
  • Deformation Resistance and Recrystallization of Commercially Pure Titanium in the High Strain Rate Hot Deformation
  • コウギョウヨウ ジュン チタン ノ ネツカン ヘンケイ テイコウ ト ネツカン

この論文をさがす

抄録

In this paper, the deformation resistance and recrystallization behavior in high temperature working (600-850°C) with high strain rates (2-150 l/s) which covers the most hot rolling conditions have been investigated.<BR>In the usual hot rolling condition the dynamic recrystallization does not occur and the resistance to hot deformation is determined by the balance between strain hardening and dynamic recovery. The flow stress sharply increases with increase in the impurity content at higher purity condition while the hardening rate due to the increase in the impurity content becomes smaller if the range exceeds a certain value. The recrystallization and grain growth behavior of commercially pure titanium is similar to that of plain carbon steels in austenite phase. In commercially pure titanium deformation bands, which act as nucleation site for recrystallization, are more easily formed than in plain carbon steels.<BR>The activation energy for hot deformation and recrystallization lies in a range between 220-260 kJ/ mol which is nearly the same for low strain rate deformation.

収録刊行物

  • 鉄と鋼

    鉄と鋼 72 (2), 321-328, 1986

    一般社団法人 日本鉄鋼協会

参考文献 (12)*注記

もっと見る

キーワード

詳細情報 詳細情報について

問題の指摘

ページトップへ