Preparation of Oxide Glasses from Metal Alkoxides by Sol-Gel Method
-
- KAMIYA Kanichi
- Department of Industrial Chemistry, Faculty of Engineeing, Mie University
-
- YOKO Toshinobu
- Department of Industrial Chemistry, Faculty of Engineeing, Mie University
-
- SAKKA Sumio
- Research Institute for Chemistry, Kyoto University
Bibliographic Information
- Other Title
-
- 金属アルコキシドを原料とするゾル・ゲル法によるガラスの製造 Si(OC2H5)4の加水分解途上で生成するシロキサンポリマの形態
- キンゾク アルコキシド オ ゲンリョウ ト スル ゾル ゲルホウ ニ ヨル ガ
- Si(OC<sub>2</sub>H<sub>5</sub>)<sub>4</sub>の加水分解途上で生成するシロキサンポリマーの形態
Search this article
Description
The type or shape of the polymers produced in the course of hydrolysis of silicontetraethoxide Si(OC2H5)4 has been investigated. Four solutions in the Si(OC2H5)4-H2O-C2H5OH-HCl system were prepared. In those solutions the molar ratios of water to Si(OC2H5)4, r, were 1.0, 2.0, 5.0 and 20.0, respectively, while the ratio of HCl to the alkoxide was kept constant at 0.01. The polymerized products or siloxane polymers were trimethylsilylated and subjected to the measurements of number-average molecular weight Mn and intrinsic viscosity [η]. Based on the relation between Mn and [η], namely, [η]=KMna where K and a are constants, type of the siloxane polymer was discussed. The exponent a's for solutions with r's of 1.0 and 2.0 were 0.75 and 0.64, respectively, showing that linear polymers are produced in those solutions. The exponent a for the solution with r of 20.0 was 0.34, corresponding to the three-dimensional or spherical polymer. Intermediate value of a was obtained for the solution with r of 5.0. These results corresponded with the authors' previous assumption that the occurrence of spinnability in a Si(OC2H5)4 solution containing a small amount of water is closely related to the formation of linear polymers in the course of hydrolysis.
Journal
-
- Journal of the Ceramic Association, Japan
-
Journal of the Ceramic Association, Japan 92 (1065), 242-247, 1984
The Ceramic Society of Japan
- Tweet
Details 詳細情報について
-
- CRID
- 1390282680192985344
-
- NII Article ID
- 110002313152
-
- NII Book ID
- AN00245650
-
- ISSN
- 18842127
- 00090255
-
- HANDLE
- 10076/11231
-
- NDL BIB ID
- 2984580
-
- Text Lang
- ja
-
- Article Type
- journal article
-
- Data Source
-
- JaLC
- IRDB
- NDL Search
- Crossref
- CiNii Articles
- OpenAIRE
-
- Abstract License Flag
- Disallowed