スラグを介してのガスから溶鉄への酸素移行速度

書誌事項

タイトル別名
  • Transfer Rate of Oxygen from Gas into Liquid Iron through Molen Slag
  • スラグ オ カイシテ ノ ガス カラ ヨウテツ エ ノ サンソ イコウ ソクド

この論文をさがす

抄録

The transfer rate of oxygen from gas phase into liquid iron through molten iron oxide-CaO-SiO2-Al2O3 slags (CaO/SiO2_??_1) at 1600°C was investigated by blowing the oxidizing gas on the slag surface which covered liquid iron. Gas blowing was started after slag was almost equilibrated with liquid iron or from non-equilibrium state.<BR>The transfer rate of oxygen into liquid iron was affected by T.Fe content in the slag. During the transfer of oxygen, FeO content in the slag largely increased, but FeO1.5 content in the slag was kept very low. When the initial T.Fe content in the slag was below equilibrium content with liquid iron, the slow deoxidation of liquid iron by the slag and an increase in FeO content in the slag occurred at first. After the FeO content increased up to its equilibrium value with oxygen in liquid iron, the transfer of oxygen into liquid iron was accelerated. A kinetic model was developed based on two films theory. The experimental results were confirmed to be interpreted by this model.

収録刊行物

  • 鉄と鋼

    鉄と鋼 85 (1), 27-33, 1999

    一般社団法人 日本鉄鋼協会

被引用文献 (1)*注記

もっと見る

参考文献 (18)*注記

もっと見る

詳細情報 詳細情報について

問題の指摘

ページトップへ