Study on the Properties of Coating Films Prepared from Metal Alkoxides
-
- YAMAMOTO Yuji
- Matsuzaka Research Center, Central Glass Co., Ltd.
-
- KAMIYA Kan-ichi
- Department of Industrial Chemistry, Faculty of Engineering, Mie University
-
- SAKKA Sumio
- Department of Industrial Chemistry, Faculty of Engineering, Mie University
Bibliographic Information
- Other Title
-
- 金属アルコキシドを用いるコーテング膜の性質に関する研究
- 金属アルコキシドを用いるコーティング膜の性質に関する研究
- キンゾク アルコキシド オ モチイル コーティング マク ノ セイシツ ニカン
Search this article
Abstract
Transparent and homogeneous coating films of the compositions SiO2, 98SiO2⋅2TiO2, 95SiO2⋅5TiO2 and 78.3SiO2⋅1.7TiO2⋅20CuO in mol% were prepared by immersing a sodalime glass substrate into metal alkoxide solutions, pulling it up, drying and heating. Effect of preparation conditions on the properties of films was examined. The time for hydrolysis of the solution, that is, interval between preparation of the solution and its application, and the drying time were varied from 1h to 2d and from 1min to 1h, respectively. The films of 0.1-0.3μm in thickness were transparent and homogeneous when the time for hydrolysis of the solution and drying time were short. The thickness of the films could be increased up to 0.5μm by adding a viscosity-increaseing agent to the solution. Defects such as crack, opaqueness or peeling off were observed when the film was thicker than 0.5μm. Scratch strength of the films was higher than that of the glass substrate and increased with increasing heating temperature and heating time. Adhesive strength of the SiO2 film was higher than 100kg/cm2.
Journal
-
- Journal of the Ceramic Association, Japan
-
Journal of the Ceramic Association, Japan 90 (1042), 328-333, 1982
The Ceramic Society of Japan
- Tweet
Details 詳細情報について
-
- CRID
- 1390282680194726272
-
- NII Article ID
- 110002312132
-
- NII Book ID
- AN00245650
-
- ISSN
- 18842127
- 00090255
- http://id.crossref.org/issn/00090255
-
- HANDLE
- 10076/11232
-
- NDL BIB ID
- 2455145
-
- Text Lang
- ja
-
- Data Source
-
- JaLC
- IRDB
- NDL
- Crossref
- CiNii Articles
-
- Abstract License Flag
- Disallowed