シリカと燐酸アルミニウムとの固溶についてクリストバライトとクリストバライト型燐酸アルミニウムとの固溶

DOI Web Site Web Site 被引用文献1件

書誌事項

タイトル別名
  • Solid Solution of Cristobalite and Cristobalite-type AlPO<sub>4</sub>
  • シリカ ト リンサン アルミニウム ト ノ コヨウ ニ ツイテ

この論文をさがす

説明

As part of the investigation of the system SiO2-Al2O3-P2O5, solid solution of SiO2 and AlPO4, both of cristobalite structure, was studied.<br>At first it was confirmed that AlPO4 can be formed from Al(OH)3 and H3PO4 by mixing and drying at 110°C. Specimens of the SiO2-AlPO4 system were prepared from mixtures of various mole ratios of Al(OH)3, SiO2 gel and H3PO4, dried and stored overnight at 110°C. After formed into tablets, the mixtures were heated at 1450°C for 2 hours.<br>Crystals of tetragonal cristobalite structure were obtained which were determined to be of homogeneous phase by X-ray diffraction, D. T. A., microscopic observation and chemical analysis, and it was confirmed that AlPO4 and SiO2 were solid-soluble in any proportions at a high temperature.<br>When increasing the amount of the substitution, the crystal structure became so disturbed that only the diffraction from (101) plane was able to be observed and the others diminished. D. T. A. peaks of α-β inversion (tetragonal-cubic inversion) which appeared sharp at the end members, became also feeble and broad and shifted toward low temperature.<br>Refractive indices by microscopic observation changed gradually with the composition of solid solutions, and at the same composition the value varied place to place in some small range, showing that the solid reaction did not proceed perfectly homogeneously.

収録刊行物

  • 窯業協會誌

    窯業協會誌 72 (822), 94-99, 1964

    公益社団法人 日本セラミックス協会

被引用文献 (1)*注記

もっと見る

詳細情報 詳細情報について

問題の指摘

ページトップへ