書誌事項
- タイトル別名
-
- Synthesis of Zinc Gallate Spinel Nanoparticles by Hydrothermal Method in the Presence of Urea and Their Sintering.
この論文をさがす
抄録
Nanometer-sized particles of zinc gallate (ZnGa2O4) spinel solid solutions over wide compositional range (Zn/Ga molar ratio = 0.341-0.499) were directly synthesized from aqueous solutions of gallium and zinc sulfates (Zn/Ga = 0.5-2.0) in the presence of urea under hydrothermal conditions at 120 to 240°C. Under almost neutral conditions in the presence of urea (pH = 7.65), zinc gallate spinel was hydrothermally formed over 200°C, although ZnCO3 and GaO(OH) were formed at 120°C. The synthesized temperature of zinc gallate spinel was able to decrease from 240 to 120°C, with the increase of the concentration of urea from 0.8 to 2.4 mol·dm-3. Zinc gallate spinel with almost stoichiometric composition (Zn/Ga = 0.499) was synthesized from the solution with Zn/Ga = 2 at 240°C. The obtained zinc gallate spinel powder was fully densified by sintering over 1200°C for 1 h.
収録刊行物
-
- Journal of the Ceramic Society of Japan (日本セラミックス協会学術論文誌)
-
Journal of the Ceramic Society of Japan (日本セラミックス協会学術論文誌) 111 (1291), 176-180, 2003
公益社団法人 日本セラミックス協会
- Tweet
詳細情報 詳細情報について
-
- CRID
- 1390282680224373632
-
- NII論文ID
- 110002292363
-
- NII書誌ID
- AN10040326
-
- ISSN
- 18821022
- 09145400
-
- NDL書誌ID
- 6473177
-
- 本文言語コード
- en
-
- データソース種別
-
- JaLC
- NDL
- Crossref
- CiNii Articles
-
- 抄録ライセンスフラグ
- 使用不可