On the Formation of the 15R-type in the β-α Transformation of SiC
-
- INOMATA Y.
- National Institute for Researches in Inorganic Materials
-
- INOUE Z.
- National Institute for Researches in Inorganic Materials
-
- KIJIMA K.
- National Institute for Researches in Inorganic Materials
Bibliographic Information
- Other Title
-
- β-SiCの加熱による構造変化と15Rの挙動
- ベータ-SiC ノ カネツ ニ ヨル コウゾウ ヘンカ ト 15R ノ キョドウ
Search this article
Abstract
The transformation of β-SiC in a high purity to α-SiC has been studied experimentally in the temperature range from 2100°C to 2300°C. The results obtained are summarized as follows:<br>1) At the initial stage of the transformation only the 6H-type was found as a newly grown phase. The 15R-type appeared always after the formation of 6H. However, the 15R thus derived disappeared with the progress of the subsequent heating. The 4H-type was not recognized throughout the present experiments.<br>2) The 6H-type has, in the range of 2100°-2300°C, a thermal stability higher than the other basic polytypes of SiC such as 3C, 4H and 15R.<br>3) The β-α transformation is considered to take place mainly through a vapour phase, because the activation energy associated with this change was estimated to be as high as 134±4kcal/mole. However, it should also be pointed out that a premonitory twinning is required to complete this transition unobstrusively.<br>4) The 15R-type is considered to grow, not direct from β-SiC, but through the 6H type already formed.<br>5) The possibility is conceived that 15R is a metastable form in the whole range of temperature. On the other hand, if a proper stable range exists for this polytype, it will be very narrow indeed, probably at about 2000°C.
Journal
-
- Journal of the Ceramic Association, Japan
-
Journal of the Ceramic Association, Japan 77 (889), 313-318, 1969
The Ceramic Society of Japan
- Tweet
Details 詳細情報について
-
- CRID
- 1390282680224538240
-
- NII Article ID
- 110002314975
-
- NII Book ID
- AN00245650
-
- ISSN
- 18842127
- 00090255
-
- NDL BIB ID
- 8468282
-
- Text Lang
- ja
-
- Data Source
-
- JaLC
- NDL
- Crossref
- CiNii Articles
-
- Abstract License Flag
- Disallowed