- Infrared Absorption of Antimonate Glass
- アンチモンガラス ノ セキガイ キュウシュウ
この論文をさがす
説明
It was confirmed that the area of the glass forming region of the system Sb2O3-Al2O3-R2O (Na2O+K2O) increases with the addition of SiO2 or GeO2.<br>The glasses containing 5% SiO2 or GeO2 melted under oxidizing condition (o. glass) gave a different infrared transmission from those melted under neutral condition (n. glass). Also the difference in such properties as the color, density, softening point, and density were observed.<br>O. glass has better infrared transmittance and chemical durability than n. glass which gave broad absorption band between 750 and 1000cm-1 and 1520cm-1. These two absorption bands at 1420cm-1, and sharp absorption bands at 1420 and 1520cm-1. These absorption bands at 1420 and 1520cm-1 appeared when o. glass is devitrified.<br>AlSbO4 crystal has the absorption band at 1420cm-1. After heating with Na2O the crystal gave a broad absorption band between 750 and 1000cm-1.<br>It was, therefore, concluded that n. glass contains the crystallite region, and the chain segments composed of Al3+Sb5+O tetrahedra are built up more easily in o. glass than in n. glass; also it may be assumed that SiO2 or GeO2 bridges the chain segment of AlSbO4 tetrahedra.
収録刊行物
-
- 窯業協會誌
-
窯業協會誌 70 (798), C199-C202, 1962
公益社団法人 日本セラミックス協会
- Tweet
詳細情報 詳細情報について
-
- CRID
- 1390282680224756736
-
- NII論文ID
- 110002302463
-
- NII書誌ID
- AN00245650
-
- ISSN
- 18842127
- 00090255
-
- NDL書誌ID
- 9214827
-
- 本文言語コード
- ja
-
- データソース種別
-
- JaLC
- NDL
- Crossref
- CiNii Articles
-
- 抄録ライセンスフラグ
- 使用不可