酸素雰囲気下におけるLiNiO2のペチーニ法合成メカニズム

LIN Shih-Pin, FUNG Kuan-Zong, HON Yi-Ming, HON Min-Hsiung

doi:10.2109/jcersj.110.1038

Pechini process was known as an excellent method for the synthesis of LiNiO₂ powder. Compared with the result of solid state reaction using NiO and Li₂CO₃ as reactants, Ni₂O₃ was the new compound found in Pechini-processed powder. In the present work, the role of Ni₂O₃ and the reaction mechanism for the synthesis of Pechini-processed LiNiO₂ were studied. XRD and DTA/TG analysis were used to investigate the phases present and the thermal reaction in the Pechini process studied. It was found that Ni₂O₃ was obtained from nickel citrate and nickel acetate which released a large amount of heat during calcination. Based on the thermodynamic calculation, Ni₂O₃ is not a stable compound in the oxidizing environment. As a result, Ni₂O₃ decomposes into NiO, and the decomposed NiO reacts with Li₂CO₃ and forms LiNiO₂ at 700°C. An isothermal kinetics study was performed on the mixture of NiO, Ni₂O₃ and Li₂CO₃ at 700°C. The result indicates that the decomposition of Ni₂O₃ into NiO takes place at the beginning hour of the isothermal reaction. Consequently, NiO and Li₂CO₃ are consumed due to the formation of LiNiO₂. Based on the results obtained, the reactions for Pechini-processed LiNiO₂ may be described by the following reactions: Citrate complex→Li₂CO₃+NiO+Ni₂O₃ Ni₂O₃→2NiO+1/2 O₂ x/2Li₂CO₃+(2-x)NiO+x/4 O₂→Li_xNi_2-xO₂+x/2 CO₂ (0<x≤1) This reaction is rationalized on the basis of the instability of Ni₂O₃ and the structural similarity between NiO and LiNiO₂.

酸素雰囲気下におけるLiNiO<sub>2</sub>のペチーニ法合成メカニズム

書誌事項

この論文をさがす

説明

収録刊行物

被引用文献 (1)*注記

参考文献 (12)*注記

キーワード

詳細情報詳細情報について

書き出し

問題の指摘