- Solidification of Glass Powder by A Hydrothermal Hot-Pressing Technique
- スイネツ ホットプレスホウ ニ ヨル ガラス フンマツ ノ コカ エイブン
この論文をさがす
説明
A borosilicate glass powder was solidified with a NaOH solution or distilled water by the hydrothermal hot-pressing technique. The effect of hydrothermal conditions on the compressive strength was investigated, and the densification mechanism of the glass powder during the hydrothermal hot-pressing was discussed in terms of isothermal shrinkage. The glass powder was successfully solidified by hydrothermal hot-pressing at a reaction temperature lower than that of an ordinary pressure sintering. The solidified body obtained in the presence of distilled water (10wt%) at 280° had a high compressive strength of about 2300kg/cm2. The analysis of initial densification process of the glass powder in hydrothermal hot-pressing with Murray's rate equation revealed that the densification proceeds both by viscous flow and by rearrangement process. Analysis of the shrinkage rates with a rate equation of hydrothermal reaction suggested that the dissolution of particles into solution controlled the initial densification of the glass powder, and that the alkaline metal acted as a catalyst.
収録刊行物
-
- 窯業協會誌
-
窯業協會誌 94 (1095), 1119-1124, 1986
公益社団法人 日本セラミックス協会
- Tweet
詳細情報 詳細情報について
-
- CRID
- 1390282680225289728
-
- NII論文ID
- 110002316783
-
- NII書誌ID
- AN00245650
-
- ISSN
- 18842127
- 00090255
- http://id.crossref.org/issn/00090255
- http://id.crossref.org/issn/09145400
-
- NDL書誌ID
- 3106736
-
- 本文言語コード
- ja
-
- データソース種別
-
- JaLC
- NDLサーチ
- Crossref
- CiNii Articles
- OpenAIRE
-
- 抄録ライセンスフラグ
- 使用不可