- An EXAFS Study of Coordination of Ag in AgI-Ag<sub>2</sub>O-GeO<sub>2</sub> Glasses
- EXAFS カイセキ ニ ヨル AgI Ag2O GeO2ケイ ガラスチュウ
この論文をさがす
抄録
Local structures around Ag+ ions in ion-conducting glasses in the system AgI-Ag2O-GeO2 were investigated by Ag K EXAFS (extended X-ray absorption fine structure) analysis. By using Ag2O and AgI crystals as reference samples, average Ag-O and Ag-I distances for three kinds of glass samples were estimated from |F(r)| curves to be 2.15-2.22Å and 2.74-2.87Å, respectively. The Ag-O atomic distances suggest that a part of Ag+ ions locate near the polygermanate anions which consisted of GeO4 tetrahedra. As the Ag+ ions of this type are strongly bonded to O2- ions, they do not contribute to the ionic conduction. It was also concluded on the basis of the Ag-I atomic distances that the rest of Ag+ ions locate at tetrahedral sites surrounded by four I- ions. Since the coodinations of these Ag+ ions are similar to those of Ag+ ions in AgI crystals which show ionic conductivity, the Ag+ ions of this type contribute to the ionic conduction.
収録刊行物
-
- 窯業協會誌
-
窯業協會誌 95 (1101), 551-555, 1987
公益社団法人 日本セラミックス協会
- Tweet
キーワード
詳細情報 詳細情報について
-
- CRID
- 1390282680225355520
-
- NII論文ID
- 110002313642
-
- NII書誌ID
- AN00245650
-
- ISSN
- 18842127
- 00090255
-
- NDL書誌ID
- 3131992
-
- 本文言語コード
- ja
-
- データソース種別
-
- JaLC
- NDL
- Crossref
- CiNii Articles
-
- 抄録ライセンスフラグ
- 使用不可