書誌事項
- タイトル別名
-
- Application of Acoustic Emission Technique to Identifying Median Crack Initiation (Part 1)
- アコースティック エミッションホウ ニ ヨル メディア ン キレツ ノ シキベ
- In Case of Soda-Lime Silicate Glass
- ソーダライムシリカガラスの場合
この論文をさがす
抄録
Crack initiations in soda-lime silicate glass during Vickers indentation were observed with an optical microscope, and the accompanied acoustic emissions (AE) were measured to evaluate KIC by the indentation micro-fracture (IM) technique. A large amount of small amplitude AE, which corresponds to the surface cracks, was detected during indentation load increment. When the load exceeded about 10kgf, penny shaped median type cracks initiated accompanied by large amplitude AE, the wave of which was composed of longitudinal wave, the reflection at the side wall of the wave guide and transversal wave. Just before the load reaching zero, lateral type cracks initiated accompanied by the large amplitude AE, in the wave of which clear longitudinal wave could not be observed. When the load was decreased before median crack initiation, the median crack initiated at the load decrement. The amplitude of the longitudinal wave (ξ) increased with increasing maximum indentation load (P). The amplitude increased also proportionaly to the crack length, which means that the energy of AE increases proportionally to the crack area.
収録刊行物
-
- 窯業協會誌
-
窯業協會誌 95 (1101), 503-508, 1987
公益社団法人 日本セラミックス協会
- Tweet
キーワード
詳細情報 詳細情報について
-
- CRID
- 1390282680225404928
-
- NII論文ID
- 110002313634
-
- NII書誌ID
- AN00245650
-
- ISSN
- 18842127
- 00090255
-
- NDL書誌ID
- 3131996
-
- 本文言語コード
- ja
-
- データソース種別
-
- JaLC
- NDL
- Crossref
- CiNii Articles
-
- 抄録ライセンスフラグ
- 使用不可