- 永山 宏
- (株) 日立製作所勝田工場検査部
書誌事項
- タイトル別名
-
- Study on Preventing Agent against Slaking of Calcia Clinker
- カルシア クリンカー ノ ショウカ ボウシザイ ニカンスルケンキュウ
この論文をさがす
抄録
In order to produce the slaking resistant calcia clinker, the additives of FeO-TiO2 system as a preventing agent against slaking have been studied. The results obtained are summarized as follows. It was recognized that optimum composition of the additives of FeO-TiO2 system effective for preventing against slaking had a tendency to remove to the TiO2 rich side in relation to increase of SiO2 content in the limestone as a raw material of calcia clinker.<br>Moreover, it was observed that SiO2, contained as an impurity in the limestone and the preventing agent against slaking, formed a high melting crystal matrix consisting with 2 CaO⋅SiO2, 3 CaO⋅SiO2 and prevented the grain growth of CaO crystals when these mixtures were burnt.<br>As a result, the increase of SiO2 content in the calcia clinker showed a deterious effect against slaking resistance.<br>Best slaking resistant clinker in this study was obtained by adding about 5% iron oxide to the limestone containing 0.3-0.4% SiO2.
収録刊行物
-
- 窯業協會誌
-
窯業協會誌 87 (1001), 28-37, 1979
公益社団法人 日本セラミックス協会
- Tweet
キーワード
詳細情報 詳細情報について
-
- CRID
- 1390282680225485312
-
- NII論文ID
- 110002316130
-
- NII書誌ID
- AN00245650
-
- ISSN
- 18842127
- 00090255
-
- NDL書誌ID
- 2040546
-
- 本文言語コード
- ja
-
- データソース種別
-
- JaLC
- NDL
- Crossref
- CiNii Articles
-
- 抄録ライセンスフラグ
- 使用不可