SiC繊維強化Si<sub>3</sub>N<sub>4</sub>複合焼結体破壊挙動のその場観察

DOI Web Site Web Site

書誌事項

タイトル別名
  • In-Situ Observation of Fracture Behavior of SiC Fiber-Si<sub>3</sub>N<sub>4</sub> Matrix Composite
  • SiC センイ キョウカ Si3N4 フクゴウ ショウケツタイ ハカイ キョド

この論文をさがす

抄録

Fracture behavior of 15vol% SiC fiber (SCS-6 Φ 140μm; AVCO Specialty Materials Div., U.S.A) reinforced Si3N4 composite materials was directly observed with an in-situ observation apparatus composed of bending machine and scanning electron microscope. When load is applied to a notched specimen, a crack initiates from the bottom of the notch and propagates in the specimen non-catastrophically, because the crack propagation is stopped successively at the fibers. With further increase of the load, the crack elongates and halts over again and again, and finally propagates along the fibers. Fatigue crack growth was not detected after 100 times of cyclic load application with a constant strain rate and 300 times application of impact load, when the maximum applied stress of the cyclic loading is less than 75% of the maximum bending strength of notched specimens. In the cyclic loading process, moreover, it was observed that the crack width becomes wide and narrow on loading and unloading, respectively.

収録刊行物

  • 窯業協會誌

    窯業協會誌 95 (1105), 869-874, 1987

    公益社団法人 日本セラミックス協会

キーワード

詳細情報 詳細情報について

問題の指摘

ページトップへ