Thermal decomposition process of Al-iso-propoxide as precursor material for alumina was analyzed with a TG-DTA apparatus. Alumina powder was prepared by calcination of the raw material in air and under reduced pressure at several temperatures. The calcined materials were identified by an X-ray powder diffraction method to be γ-alumina below 900°C and α-alumina above 1100°C, of which crystal structures were independent of the atmospheric environment. The powder briquettes were made by a CIP (cold isostatic pressing) method, which were sintered in the temperature range of 1600° to 1800°C. The sinterabilities of alumina were discussed relative to the effects of atmosphere, crystal system, calcination temperature, and firing temperature.
収録刊行物
-
- 窯業協會誌
-
窯業協會誌 95 (1104), 828-830, 1987
公益社団法人 日本セラミックス協会
- Tweet
詳細情報 詳細情報について
-
- CRID
- 1390282680225665792
-
- NII論文ID
- 110002313697
-
- NII書誌ID
- AN00245650
-
- ISSN
- 18842127
- 00090255
-
- NDL書誌ID
- 3144034
-
- 本文言語コード
- ja
-
- データソース種別
-
- JaLC
- NDL
- Crossref
- CiNii Articles
-
- 抄録ライセンスフラグ
- 使用不可