Si<sub>3</sub>N<sub>4</sub>反応焼結体と溶鉄との反応における溶鉄中の溶解酸素の影響

DOI Web Site Web Site 被引用文献7件

書誌事項

タイトル別名
  • Influence of Dissolved Oxygen on the Reaction between Molten Iron and Reaction-Bonded Si<sub>3</sub>N<sub>4</sub>
  • Si3N4 ハンノウ ショウケツタイ ト ヨウテツ ト ノ ハンノウ ニ オケ

この論文をさがす

抄録

Fundamental investigations of the reaction between Si3N4 and molten iron have shown that Si3N4 material is desirable in steelmaking process. This paper describes the influence of dissolved oxygen in iron on the corrosion of reaction-bonded Si3N4. The results are as follows:<br>Si3N4 specimens dipped into iron containing more-than-300-ppm dissolved oxygen for 30 minutes at 1630°C and rotated at 300rpm were not attacked. However, molten iron of less-than-300-ppm oxygen attacked Si3N4 as oxygen contents decreased. Optical microscope and EPMA observations showed the formation of 50-150-μm thick SiO2 layer on the Si3N4 surface which did not corrode. Otherwise, there was none of the thick layer on specimens dipped in below-300-ppm-oxygen iron. This reaction mechanism was discussed thermodynamically. Iron with a high dissolved oxygen level forms a large amount of SiO2 at the beginning of the reaction, which acts as a protection layer on the Si3N4 surface. On the other hand, a low dissolved oxygen level iron causes the Si of Si3N4 to dissolve into iron without SiO2 formation.

収録刊行物

  • 窯業協會誌

    窯業協會誌 95 (1107), 1047-1052, 1987

    公益社団法人 日本セラミックス協会

被引用文献 (7)*注記

もっと見る

キーワード

詳細情報 詳細情報について

問題の指摘

ページトップへ