Preparation of Cordierite/ZrO2 Nano-Composite Powders by a Colloidal Coating Process.
-
- SUN En-Hai
- Institute of Scientific and Industrial Research, Osaka University
-
- KUSUNOSE Takafumi
- Institute of Scientific and Industrial Research, Osaka University
-
- SEKINO Tohru
- Institute of Scientific and Industrial Research, Osaka University
-
- ADACHI Tomohiko
- Institute of Scientific and Industrial Research, Osaka University
-
- WADA Masashi
- Institute of Scientific and Industrial Research, Osaka University
-
- NIIHARA Koichi
- Institute of Scientific and Industrial Research, Osaka University
Bibliographic Information
- Other Title
-
- コロイダルコーティングによるコーディエライト/ZrO<sub>2</sub>ナノコンポジットパウダーの作製
- Preparation of Cordierite/ZnO2 Nano-Composite Powders by a Colloidal Coating Process
Search this article
Abstract
Cordierite/ZrO2 nano-composite powders were prepared by a colloidal coating process. Cordierite particles are embedded within a continuous layer of fine amorphous ZrO2 that was provided by the colloidal processing after drying. Tetragonal ZrO2 was first formed at 650°C and monoclinic ZrO2 phase was identified at the calcination temperature of 800°C. After calcination at 850°C, crystallized ZrO2 particles with the size from 10nm to 30nm homogeneously covered the surface of cordierite particles. Cordierite/ZrO2 nano-composite powders prepared by a colloidal coating process show better sinterability than that of cordierite/ZrO2 powder mixtures prepared by a conventional mixing method, and were sintered to a density of over 96% at a low temperature of 1300°C.
Journal
-
- Journal of the Ceramic Society of Japan
-
Journal of the Ceramic Society of Japan 110 (1278), 92-97, 2002
The Ceramic Society of Japan
- Tweet
Keywords
Details 詳細情報について
-
- CRID
- 1390282680225875968
-
- NII Article ID
- 110002291558
-
- NII Book ID
- AN10040326
-
- ISSN
- 18821022
- 09145400
-
- NDL BIB ID
- 6049975
-
- Text Lang
- en
-
- Data Source
-
- JaLC
- NDL
- Crossref
- CiNii Articles
-
- Abstract License Flag
- Disallowed