ホットプレス法により作製した LaPO<sub>4</sub> 被覆アルミナ繊維/アルミナマトリックス複合材の 高温機械的性質

DOI Web Site Web Site 参考文献38件 オープンアクセス

書誌事項

タイトル別名
  • Fracture Behavior of Monazite-Coated Alumina Fiber-Reinforced Alumina-Matrix Composites at Elevated Temperature

この論文をさがす

説明

High-temperature strength, fracture behavior and microstructure were observed for monazite-coated alumina fiber-reinforced alumina matrix composites hot-pressed at 1200-1300°C. The composites with 27-41 vol% alumina fiber showed no significant change in strength at 25-1100°C. However, the strength of the composites decreased markedly at a test temperature higher than 1100°C. The composites hot-pressed at a temperature lower than 1250°C fractured in a pseudoductile manner in the test temperature range from 25°C to 1100°C. Young's modulus of the elastic region decreased with increasing test temperature. These composites showed larger deformation at a test temperature above 1100°C. On the other hand, the composites hot-pressed at more than 1250°C fractured in a brittle manner at 25°C-1200°C of test temperature. The fracture energy of the composite increased with increasing test temperature and decreased with sintering temperature.<br>

収録刊行物

参考文献 (38)*注記

もっと見る

キーワード

詳細情報 詳細情報について

問題の指摘

ページトップへ