- The Crystal Growth of Diopside Using NaCl
- エンカ ナトリウム オ モチイタ ディオプサイド ノ ケッショウ セイチョウ
この論文をさがす
抄録
Diopside (CaO⋅MgO⋅2SiO2) crystals have been grown in molten alkali halides. Natural dolomite (CaCO3⋅MgCO3) and α-quartz were found to be the best starting materials, NaCl being the most suitable flux. Characterization has been made with crystals obtained under the following conditions: R1=α-quartz/dolomite (molar ratio), R2=starting material/flux (weight ratio), soaking temperature and soaking period. When soaked at 1100°C for 12h with R2=0.02, the following results were obtained.<br>(1) Monticellite (CaO⋅MgO⋅SiO2) was synthesized with 0.25≤R1≤1.00, åkermanite (2CaO⋅MgO⋅2SiO2) with 0.75≤R1≤1.75 and diopside, with 1.25≤R1≤3.00.<br>(2) The well grown diopside crystals had a maximum size of 2.0×1.5×0.5mm (plate), 1.0×1.0×0.8mm (polyhedron), φ0.3×4.0mm (needle).
収録刊行物
-
- 窯業協會誌
-
窯業協會誌 93 (1079), 376-381, 1985
公益社団法人 日本セラミックス協会
- Tweet
キーワード
詳細情報 詳細情報について
-
- CRID
- 1390282680226565504
-
- NII論文ID
- 110002313408
-
- NII書誌ID
- AN00245650
-
- ISSN
- 18842127
- 00090255
-
- NDL書誌ID
- 3044651
-
- 本文言語コード
- ja
-
- データソース種別
-
- JaLC
- NDL
- Crossref
- CiNii Articles
-
- 抄録ライセンスフラグ
- 使用不可