Preparation of Silica-Pillared Fluorohectorite by Cointercalation of Polysiloxane and Polyvinyl Alcohol

DOI Web Site Web Site 38 References
  • NAKAO Toshiaki
    Aichi Industrial Technology Institute Department of Material Science and Engineering, Nagoya Institute of Technology
  • NOGAMI Masayuki
    Department of Material Science and Engineering, Nagoya Institute of Technology

Bibliographic Information

Other Title
  • ポリシロキサンとポリビニルアルコールの同時インターカレーションによる シリカ架橋フッ素ヘクトライトの合成

Search this article

Abstract

Silica-pillared clays with mesopores were prepared from fluorohectorite, aminopropyltriethoxysilane (APS) and tetraethoxysilane (TEOS) affected using polyvinyl alcohol (PVA). The presence of PVA was important in this synthesis and was effective on the porosity of the obtained silica-pillared clays. Based on the X-ray diffraction measurements, the basal spacings of the silica-pillared clays increased from 1.7 to 5.6 nm with an increase in the PVA concentration. As with the basal spacings, the peaks of the pore size distribution and the average pore diameter shifted up to approximately 3 nm. The pore volumes corresponded to the basal spacings expanded by cointercalation of PVA and polysiloxane. The pore properties and structures of the pillared clays were investigated and the results indicated the relation between the layer structure and pore structure.<br>

Journal

References(38)*help

See more

Keywords

Details 詳細情報について

Report a problem

Back to top