Effect of Heat-Treatment Temperature on Optical Properties of Ba2TiSi2O8 Nanocrystallized Glasses

DOI Web Site Web Site 11 Citations 46 References Open Access

Bibliographic Information

Other Title
  • Ba<sub>2</sub>TiSi<sub>2</sub>O<sub>8</sub> ナノ結晶化ガラスの光学特性に及ぼす熱処理温度の影響

Search this article

Description

Nanocrystallized glasses with the composition of 40BaO•20TiO2•40SiO2, stoichiometric to fresnoite (Ba2TiSi2O8), have been prepared by heat-treatment at various temperatures, and their optical properties, second-harmonic generation (SHG) and photoluminescence (PL), have been examined. The glass subjected to the heat-treatment at 760°C for 1 h showed a dense formation of Ba2TiSi2O8 crystals with the dimension of 200-300 nm, and maintained a visual transparency. Visible green light corresponding to SHG at 532 nm was confirmed in the transparent Ba2TiSi2O8 nanocrystallized glasses. The maximum second-harmonic intensity in the nanocrystallized samples was on the order of 1/100 when compared to that of an α-quartz single crystal. Furthermore, the bluish white PL with a peak at the wavelength of about 470 nm was also visually observed in samples heat-treated at 750-800°C.<br>

Journal

Citations (11)*help

See more

References(46)*help

See more

Keywords

Details 詳細情報について

Report a problem

Back to top