- Properties of Anatase Films for Photocatalyst from Peroxotitanic Acid Solution and Peroxo-Modified Anatase Sol
- Properties of Anatase Films for Photoca
この論文をさがす
説明
Anatase films for a photocatalyst have been prepared on substrates by a dip-coating technique using peroxotitanic acid (PTA) solution and peroxo-modified anatase (PA) sol. The as-dried film prepared from PA sol had already crystallized to anatase phase, while the film prepared from PTA solution crystallized above 300°C. Adhesion strength of the films at 300°C was over 60MPa, and their relative density was over 80%. Photocatalytic efficiency of the film prepared from PA sol for the degradation of acetic acid was higher than that of the film prepared from PTA solution. The films obtained above 300°C from PA sol exhibited the highest catalytic activity. However, the film less than 0.70μm thick resulted in decrease of photocatalysis.
収録刊行物
-
- Journal of the Ceramic Society of Japan (日本セラミックス協会学術論文誌)
-
Journal of the Ceramic Society of Japan (日本セラミックス協会学術論文誌) 104 (1214), 914-917, 1996
公益社団法人 日本セラミックス協会
- Tweet
キーワード
詳細情報 詳細情報について
-
- CRID
- 1390282680255608448
-
- NII論文ID
- 110002291371
-
- NII書誌ID
- AN10040326
-
- ISSN
- 18821022
- 09145400
- http://id.crossref.org/issn/09145400
-
- NDL書誌ID
- 4047279
-
- データソース種別
-
- JaLC
- NDLサーチ
- Crossref
- CiNii Articles
-
- 抄録ライセンスフラグ
- 使用不可