Characteristics of size controlled hydroxyapatite powders with nanometer size prepared by flame spray pyrolysis
-
- CHO Jung Sang
- Department of Chemical Engineering, Konkuk University
-
- KO You Na
- Department of Chemical Engineering, Konkuk University
-
- JUNG Dae Soo
- Department of Chemical Engineering, Konkuk University
-
- JANG Hee Chan
- Department of Chemical Engineering, Konkuk University
-
- LEE Man-Jong
- Department of Advanced Technology Fusion, Konkuk University
-
- KANG Yun Chan
- Department of Chemical Engineering, Konkuk University
この論文をさがす
抄録
Size controlled hydroxyapatite powders with nanometer sizes were directly prepared by high temperature flame spray pyrolysis. Nanosized hydroxyapatite powders were formed from the evaporated vapors by chemical vapor deposition process. The composition ratio of calcium and phosphorous components was 1.67. The mean size of the hydroxyapatite powders increased from 21 to 81 nm when the concentration of spray solution was changed from 0.05 to 2 mol/L. Sintering of the nanosized hydroxyapatite powders occurred at a temperature of 1000°C, and grain growth increased with increasing the sintering temperatures. The mean grain sizes of the pellets sintered at temperatures of 1200, 1300, and 1400°C were 0.93, 4.9, and 18 μm.
収録刊行物
-
- Journal of the Ceramic Society of Japan
-
Journal of the Ceramic Society of Japan 117 (1370), 1060-1064, 2009
公益社団法人 日本セラミックス協会
- Tweet
詳細情報 詳細情報について
-
- CRID
- 1390282680259242624
-
- NII論文ID
- 130000304920
-
- NII書誌ID
- AA12229489
-
- ISSN
- 13486535
- 18820743
-
- NDL書誌ID
- 10374089
-
- 本文言語コード
- en
-
- データソース種別
-
- JaLC
- NDL
- Crossref
- CiNii Articles
-
- 抄録ライセンスフラグ
- 使用不可