Formation of BaMgAl10O17:Eu Phosphor Particles with Spherical Shape and Filled Morphology in the Flame Spray Pyrolysis

DOI Web Site Web Site 被引用文献1件 参考文献25件

この論文をさがす

抄録

Fine-sized, spherical BaMgAl10O17:Eu2+ phosphor particles with filled morphologies were prepared by flame spray pyrolysis. Precursor particles prepared by flame spray pyrolysis at a low-temperature diffusion flame and a short particle residence time within the diffusion flame were of large size and had hollow structures. On the other hand, precursor particles prepared at optimum preparation conditions were fine sized, had filled structures, and narrow size distributions. The melting of large-sized intermediate particles with hollow structures within the high-temperature diffusion flame formed fine-sized, spherical precursor particles with filled structures. The BaMgAl10O17:Eu2+ phosphor particles prepared by flame spray pyrolysis at optimum preparation conditions were fine-sized and had regular morphologies after post-treatment at 1400°C. The mean size of the BaMgAl10O17:Eu2+ phosphor particles was 1.0 μm. The photoluminescence intensity of fine-sized, spherical BaMgAl10O17:Eu2+ phosphor particles with filled structures was higher than that of large-sized phosphor particles with hollow structures excited by the vacuum ultraviolet light at the wavelength, 147 nm.<br>

収録刊行物

被引用文献 (1)*注記

もっと見る

参考文献 (25)*注記

もっと見る

キーワード

詳細情報 詳細情報について

問題の指摘

ページトップへ