Hydroxyapatite ceramics coating on magnesium alloy via a double layered capsule hydrothermal hot-pressing
-
- ONOKI Takamasa
- Department of Materials Science, Graduate School of Engineering, Osaka Prefecture University
-
- YAMAMOTO Shin-ya
- Department of Materials Science, Graduate School of Engineering, Osaka Prefecture University
この論文をさがす
抄録
Hydroxyapatite (HA: Ca10(PO4)6(OH)2) ceramic coating on magnesium (Mg) alloy (AZ31; Mg–3Al–1Zn) was achieved simultaneously by using a double layered capsule hydrothermal hot-pressing (DC-HHP) method at the low temperature as low as 150°C with no special surface treatment on the surface of the Mg alloy. A mixture of calcium hydrogen phosphate dehydrate (DCPD) and calcium hydroxide (Ca(OH)2) was used as a starting powder material for solidifying HA. Pull-out tests were conducted in order to obtain an estimate of adhesive properties for the HA coating to the Mg alloy. Average value of maximum shear stress was determined to 6.1 ± 1.0 MPa. After the pull-out fracture tests, it was revealed that HA ceramics remained on the surface of the Mg alloy. The Mg alloy could be bonded to HA ceramics with good adhesive properties.
収録刊行物
-
- Journal of the Ceramic Society of Japan
-
Journal of the Ceramic Society of Japan 118 (1380), 749-752, 2010
公益社団法人 日本セラミックス協会
- Tweet
詳細情報 詳細情報について
-
- CRID
- 1390282680262358016
-
- NII論文ID
- 130000304631
-
- NII書誌ID
- AA12229489
-
- ISSN
- 13486535
- http://id.crossref.org/issn/13486535
- 18820743
-
- NDL書誌ID
- 10770857
-
- 本文言語コード
- en
-
- データソース種別
-
- JaLC
- NDL
- Crossref
- CiNii Articles
-
- 抄録ライセンスフラグ
- 使用不可