Preparation of nanosized aluminum nitride powders by the cyanonitridation method

DOI Web Site Web Site 参考文献13件
  • JUNG Woo-Sik
    School of Chemical Engineering, College of Engineering, Yeungnam University

この論文をさがす

説明

Nanosized aluminum nitride (AlN) powders were prepared by calcining δ-alumina (δ-Al2O3) nanopowders under a flow of acetonitrile (CH3CN) diluted in argon. The nitridation process of δ-Al2O3 to AlN was monitored by powder X-ray diffraction patterns and 27Al magic-angle spinning nuclear magnetic resonance spectroscopy. δ-Al2O3 began to be converted to AlN at 1050°C without δ-α alumina transformation and the conversion was completed at 1300°C. The cyanide radical, which was produced by thermal decomposition of CH3CN, reacted with Al2O3 to form AlN. The cyanonitridation method can considerably mitigate the two main drawbacks of the carbothermal reduction and nitridation method: high reaction temperature and intimate mixing of Al2O3 with carbon. Cathodoluminescence spectra of the nanosized AlN powders obtained in this study showed an intense ultraviolet emission band at 376 nm.

収録刊行物

参考文献 (13)*注記

もっと見る

キーワード

詳細情報 詳細情報について

問題の指摘

ページトップへ