Afterglow luminance property of phosphorescent phosphor SrAl2O4:Eu2+,Dy3+-glass composites
-
- YOSHIDA Hideki
- Ceramic Research Center of Nagasaki
-
- FUJINO Shigeru
- Department of Chemical Engineering, Faculty of Engineering, Kyushu University
-
- KAJIWARA Toshihisa
- Department of Chemical Engineering, Faculty of Engineering, Kyushu University
Search this article
Abstract
The effect of mixing ratio, firing temperature and matrix glass composition on afterglow luminance property of SrAl2O4:Eu2+,Dy3+-glass composites were investigated. As a result, the brightness showed a maximum at 35 mass % of the mixing ratio of the phosphor for the glass and 780°C of the firing temperature. And it was increased with decreasing the Na2O content of the matrix glass. From the backscattered electron and the EDX analysis, it is thought that the intermediate layers generated between the phosphors and the Na2O-poor matrix glass work as antireflective and the phosphor particles in the composite emit phosphorescent light more efficiently. As higher the basicity parameter, B, the intermediate layer was clearer, which means that the reactivity at the phosphor/glass boundaries was lower, and the narrow reaction layers was formed.
Journal
-
- Journal of the Ceramic Society of Japan
-
Journal of the Ceramic Society of Japan 118 (1381), 784-787, 2010
The Ceramic Society of Japan
- Tweet
Keywords
Details 詳細情報について
-
- CRID
- 1390282680263369728
-
- NII Article ID
- 130000333468
-
- NII Book ID
- AA12229489
-
- ISSN
- 13486535
- 18820743
-
- NDL BIB ID
- 10801543
-
- Text Lang
- en
-
- Data Source
-
- JaLC
- NDL
- Crossref
- CiNii Articles
-
- Abstract License Flag
- Disallowed