- Evaluation valuation of Anisotropy Field and g-factor of c-plane Oriented CoPtCr Alloy Film Using Q-band Ferromagnetic Resonance
- Qバンド キョウジセイ キョウメイ オ モチイタ cメンハイコウ CoPtCr ゴウキン ハクマク ノ イホウセイ ジカイ オヨビ g インシ ノ ヒョウカ
この論文をさがす
抄録
The uniaxial magnetic anisotropy field, Hk, and g-factor of a c-plane oriented CoPtCr alloy film was quantitatively evaluated by using Q-band (∼34 GHz) ferromagnetic resonance (FMR). An FMR signal with a high signal-to-noise ratio was successfully obtained by using a 2mmφ-Macor holder, which achieves phase matching, a decrease in the background of the signal, and accurate alignment of the external field parallel to the film normal or in-plane. An external field was applied perpendicularly or horizontally to the film, and a single magnetic domain was maintained during the measurements. The measured FMR signals demonstrated that 1) the Hk and g-factor were simultaneously derived for CoPtCr films with Co 75-90 at.%, 2) the magnitude of Hk was supported by that obtained with a Torque magnetometer, and 3) the g-factor increased from 2.11 to 2.19 when Co content was decreased from 85 to 65 at.% and the Cr content was increased from 5 to 20 at.%.
収録刊行物
-
- Journal of the Magnetics Society of Japan
-
Journal of the Magnetics Society of Japan 34 (3), 214-219, 2010
公益社団法人 日本磁気学会
- Tweet
詳細情報 詳細情報について
-
- CRID
- 1390282680263400960
-
- NII論文ID
- 130000262854
-
- NII書誌ID
- AA12297999
-
- ISSN
- 18822932
- 18822924
-
- NDL書誌ID
- 10695158
-
- 本文言語コード
- ja
-
- データソース種別
-
- JaLC
- NDL
- Crossref
- CiNii Articles
-
- 抄録ライセンスフラグ
- 使用不可