- YANG Jun
- Department of Chemistry, Jinan University
-
- LI Runsheng
- Department of Chemistry, Jinan University Guangzhou No.2 Middle School
-
- LI Xiaoci
- Department of Chemistry, Jinan University
-
- LONG Yulin
- Department of Chemistry, Jinan University
-
- ZHOU Junyi
- Department of Chemistry, Jinan University
-
- ZHANG Yuanming
- Department of Chemistry, Jinan University
この論文をさがす
抄録
Pure perovskite compound SrFeO3 nanocrystals were successfully synthesized in molten NaNO3–KNO3 eutectic with Na2O2 from a mixture of strontium nitrate and ferric nitrate. The effect of metal precursors, salt medium, annealing temperature (mainly 400–800°C), and oxidizing properties of the melt on the phase composition, crystallite size and morphology of the resulting metal oxides were systematically studied by simultaneous TG/DSC, X-ray diffraction (XRD), scanning electron microscopy (SEM) methods. The results showed that the formation of the SrFeO3 phase mainly depended on the nature of the metal precursor and salt medium. It was found that metal nitrates are the suitable precursors and NaNO3–KNO3 eutectic with Na2O2 is the suitable salt medium, which results in the formation of pure SrFeO3 nanocrystals at a much lower temperature of 400°C.
収録刊行物
-
- Journal of the Ceramic Society of Japan
-
Journal of the Ceramic Society of Japan 119 (1394), 736-739, 2011
公益社団法人 日本セラミックス協会
- Tweet
詳細情報 詳細情報について
-
- CRID
- 1390282680263788544
-
- NII論文ID
- 130001091516
-
- NII書誌ID
- AA12229489
-
- ISSN
- 13486535
- 18820743
-
- NDL書誌ID
- 11255857
-
- 本文言語コード
- en
-
- データソース種別
-
- JaLC
- NDL
- Crossref
- CiNii Articles
-
- 抄録ライセンスフラグ
- 使用不可