Thermoelectric properties and thermopower enhancement of Al-doped ZnO with nanosized pore structure

DOI 機関リポジトリ (HANDLE) Web Site Web Site 被引用文献7件 参考文献10件 オープンアクセス
  • OHTAKI Michitaka
    Department of Molecular and Material Sciences, Interdisciplinary Graduate School of Engineering Sciences, Kyushu University
  • ARAKI Kazuhiko
    Department of Molecular and Material Sciences, Interdisciplinary Graduate School of Engineering Sciences, Kyushu University

この論文をさがす

説明

Thermoelectric properties of Al-doped ZnO (Zn0.98Al0.02O) with nanosized pore (nanovoid) structure were investigated. Nanovoids were formed by using monodisperse polymethylmethacrylate (PMMA) particles of 150, 425, and 1800 nm in average diameter as a void forming agent (VFA). Whereas the thermal conductivity of the samples sintered with the 150 nm PMMA particles of 5–10 wt % was efficiently suppressed, the magnitude of the suppression was almost the same as that of the electrical conductivity, revealing that the selective phonon scattering was failed in these samples. However, being helped by the contribution from an enhancement in the Seebeck coefficient, the samples sintered with 5–10 wt % of 150 nm VFA successfully attained the ZT values of 0.55–0.57 at 1000°C. Furthermore, the reduction of the thermal conductivity with increasing porosity was much steeper than ordinary porous materials, suggesting significantly stronger phonon scattering by the nanosized pore structure.

収録刊行物

被引用文献 (7)*注記

もっと見る

参考文献 (10)*注記

もっと見る

キーワード

詳細情報 詳細情報について

問題の指摘

ページトップへ