Fabrication of β-SiC micropatterns from a facile replication process

DOI Web Site Web Site 参考文献23件
  • ZHANG Kuibao
    State Key Laboratory of Advanced Technology for Materials Synthesis and Processing, Wuhan University of Technology
  • OKUMURA Masatoshi
    Extreme Energy-Density Research Institute, Nagaoka University of Technology
  • NAKAYAMA Tadachika
    Extreme Energy-Density Research Institute, Nagaoka University of Technology
  • SUZUKI Tsuneo
    Extreme Energy-Density Research Institute, Nagaoka University of Technology
  • SUEMATSU Hisayuki
    Extreme Energy-Density Research Institute, Nagaoka University of Technology
  • NIIHARA Koichi
    Extreme Energy-Density Research Institute, Nagaoka University of Technology
  • FU Zhengyi
    State Key Laboratory of Advanced Technology for Materials Synthesis and Processing, Wuhan University of Technology

書誌事項

タイトル別名
  • Fabrication of .BETA.-SiC micropatterns from a facile replication process
  • Fabrication of v SiC micropatterns from a facile replication process

この論文をさがす

抄録

Fine-structured β-SiC ceramic patterns were successfully fabricated from a facile replication route using Si mold as the master structure, PVA as the binding agent and nanosized β-SiC powder as the raw material. After slurry deposition and drying, the patterns were integrally transferred from the Si mold to the coating samples. The intact micropatterns were maintained up to 1500°C without obvious shrinkage. The samples exhibit nearly net-sized feature of 1.7 µm after drying and sintering. This net-sized structure is a great advantage of β-SiC patterns over the counterparts of oxide ceramic materials. All samples are in nanosized porous structure with narrowly distributed pore sizes.