FATIGUE CRACK INITIATION-PROPAGATION AND STRENGTH OF OUT-OF-PLANE GUSSET WELDED JOINTS UNDER COMPRESSIVE CYCLIC STRESSES

DOI Web Site 1 Citations Open Access
  • MORI Takeshi
    法政大学 都市環境デザイン工学科
  • KIMURA Naoto
    法政大学大学院 デザイン工学研究科都市環境デザイン工学専攻

Bibliographic Information

Other Title
  • 圧縮繰返し応力を受ける面外ガセット溶接継手の疲労き裂発生・進展挙動と疲労強度

Description

 Fatigue tests have been carried out on out-of-plane gusset welded joint specimens under axially pulsating compressive stresses, reversed stresses and pulsating tensile stresses in order to clarify the fatigue crack initiation and propagation behavior, and fatigue strength under compressive cyclic stresses. In the fatigue tests, the multiple repeated two-step stress tests have been also performed for the purpose of leaving beach marks in a fatigue failure surface in addition to the constant amplitude stress tests. The fatigue test results suggest that the fatigue crack stops propagating under the pulsating compressive stresses after the crack penetrates the main plates and extends to a certain extent, the fatigue strength and propagation behavior before it penetrates the plate under the pulsating compressive stresses are the same as those under the pulsating tensile stresses.

Journal

Citations (1)*help

See more

Related Projects

See more

Keywords

Details 詳細情報について

Report a problem

Back to top