変調構造からの微細混合組織の形成と超塑性

DOI Web Site

書誌事項

タイトル別名
  • Formation of Microduplex Structure and Superplasticity in a Cu-26Ni-8Fe Alloy
  • ヘンチョウ コウゾウ カラ ノ ビサイ コンゴウ ソシキ ノ ケイセイ ト チ

この論文をさがす

抄録

A supersaturated Cu-26Ni-8Fe alloy was deformed by cold rolling and the changes occurring on annealing at 750°C have been follovred by hardness testing and optical and electron microscopy observation. It was found that a modulated structure formed prior to recrystallization of a supersaturated solid solution. In the case of the heavily deformed sample, the iron nickel-rich phases grow anywhere including grain boundaries or deformation bands, and the recrystallization can start in the area free of the modulated structure around the coagulated iron nickel-rich phases. Therefore, the recrystallized structure consists of fine equiaxed copper-rich and iron nickel-rich grains termed as the microduplex structure. The structure has a good strength and ductility at room temperature. The structure also has a suitable high temperature stability and so appears capable of undergoing superplastic deformation at 750°C. The strain rate sensitivity index of flow stress m of about 0.5 was obtained and the specimen maintained a relatively fine equiaxed grain structure even after large elongation at 750°C.

収録刊行物

  • 材料

    材料 30 (338), 1083-1087, 1981

    公益社団法人 日本材料学会

キーワード

詳細情報 詳細情報について

問題の指摘

ページトップへ