- Environmental cracking characteristics of deep-drawn austenitic stainless steel cases.
- オーステナイトケイ ステンレス コウシボリ キョウタイ ノ カンキョウ ワレ
この論文をさがす
抄録
Environmental cracking tests for deep-drawn austenitic stainless steel cases were carried out in standing water in a manhole and under accelerated conditions, to test for hydrogen embrittlement. The main results are as follows.<br>(1) 8.6% and 9.1% Ni austenitic stainless steel cases with a sacrificial zinc electrode became cracked after setting for several months in standing water in a manhole. The electrochemical condition was -790mV at the lowest electrode potential, and a current density of 50mA/m2.<br>(2) 8.6%, 9.1% and 10% Ni austenitic stainless steel cases became cracked under accelerated conditions, to test for hydrogen embrittlement. The electrochemical conditions were the same for those cases with a sacrificial zinc electrode in sea water. However, 12% Ni austenitic stainless steel case did not become cracked under these conditions.<br>(3) Susceptibility to hydrogen embrittlement depended on the ratio of residual stress to tensile strength, and on martensite content. Thus, the cracking probability of deep-drawn cases in this environment could be estimated.<br>(4) Stable austenitic stainless steel cases did not became cracked after more than 7 years in these manholes.
収録刊行物
-
- 材料
-
材料 39 (439), 432-437, 1990
公益社団法人 日本材料学会
- Tweet
詳細情報 詳細情報について
-
- CRID
- 1390282680368044416
-
- NII論文ID
- 110002297593
-
- NII書誌ID
- AN00096175
-
- ISSN
- 18807488
- 05145163
-
- NDL書誌ID
- 3661101
-
- 本文言語コード
- ja
-
- データソース種別
-
- JaLC
- NDL
- Crossref
- CiNii Articles
-
- 抄録ライセンスフラグ
- 使用不可