- The influence of moisture in air on fatigue crack propagation characteristics of high-strength steels.
- コウ キョウド コウ ノ ヒロウ キレツ シンテン ニ オヨボス タイキチュウ
この論文をさがす
抄録
In order to clarify the influence of moisture in air on fatigue crack propagation characteristics of high strength steels, fatigue tests were conducted in laboratory air and dry air using CT specimens.<br>The following results were obtained:<br>(1) In case of low stress ratio (R=0.1), the retardation-effect by moisture in air was recognized in low ΔK region (stage 2a) of the specimen whose tensile strength was below about 2000MPa. This behavior was explained due to the oxide-induced crack closure promoted by moisture in air.<br>(2) In case of high stress ratio (R=0.8), the acceleration-effect by moisture in air was recognized in the medium ΔK region (stage 2b) of the specimen whose tensile strength was higher than 1000MPa. This acceleration-effect might be caused by the hydrogen embrittlement which occurred near the specimen surface, and became more remarkable when the test frequency was low.
収録刊行物
-
- 材料
-
材料 39 (439), 425-431, 1990
公益社団法人 日本材料学会
- Tweet
キーワード
詳細情報 詳細情報について
-
- CRID
- 1390282680368841728
-
- NII論文ID
- 110002297592
-
- NII書誌ID
- AN00096175
-
- COI
- 1:CAS:528:DyaK3cXks1egsr0%3D
-
- ISSN
- 18807488
- 05145163
- http://id.crossref.org/issn/05145163
-
- NDL書誌ID
- 3661137
-
- 本文言語コード
- ja
-
- データソース種別
-
- JaLC
- NDL
- Crossref
- CiNii Articles
-
- 抄録ライセンスフラグ
- 使用不可