高マンガン鋼の疲労強度と微視的き裂の発生

DOI Web Site

書誌事項

タイトル別名
  • Fatigue Strength of High Mn Non-Magnetic Steel and Its Microscopic Characteristics.
  • コウ マンガン コウ ノ ヒロウ キョウド ト ビシテキ キレツ ノ ハッセイ

この論文をさがす

抄録

Fatigue behavior of high manganese non-magnetic austenitic steel (HM steel) was studied through the rotating bending fatigue tests using plain specimens with a partial shallow notch by means of the successive-taken replica method. This behavior was compared with that of an austenitic stainless steel (SUS304). The experimental results showed that the fatigue limit of HM steel was the same as that of SUS304, and distinct knee point was observed in S-N curve of both materials. It was found that the fatigue cracks of these materials initiated at grain boundaries or in its neighborhood.<br>It was apparently observed that some non-propagating micro-cracks existed in the specimen surface of HM steel subjected to the stress cycling of fatigue limit by 107 cycles, while no micro-crack existed in the specimen of SUS304 subjected to the same stress condition.

収録刊行物

  • 材料

    材料 43 (486), 324-328, 1994

    公益社団法人 日本材料学会

キーワード

詳細情報 詳細情報について

問題の指摘

ページトップへ