アルミニウム合金の二段多重変動荷重下での疲労き裂進展挙動について　　変動荷重レベルがともに疲労き裂進展曲線の第ＩＩ領域にある場合

DOI Web Site 被引用文献1件

書誌事項

タイトル別名
  • Fatigue crack growth behavior of aluminum alloy under repeated two-step load conditions. The case where both stress levels KH and KL are in region II of crack growth rate curve.
  • アルミニウム ゴウキン ノ 2ダン タジュウ ヘンドウ カジュウカ デ ノ ヒ
  • The Case where Both Stress Levels <i>K</i><sub>H</sub> and <i>K</i><sub>L</sub> are in Region II of Crack Growth Rate Curve
  • 変動荷重レベルがともに疲労き裂進展曲線の第II領域にある場合

この論文をさがす

抄録

Aluminum alloy (A2017-T3) compact tension specimens were tested under repeated two-step load conditions, and the crack growth rate and crack closure behavior were observed. The higher and lower stress levels, KH and KL, were selected in the region II of the crack growth rate curve of the material obtained by ΔK increasing tests. It was found that the crack growth rate da/dN and crack opening stress intensity Kop were affected by the stress cycle ratio KL/NH; namely, da/dN was decreased and Kop was raised by the increase of NL/NH. The estimation of the crack growth rate for lower stress level KL by the linear cummulative law shows that the estimated relation of (da/dN)L versus (Keff)L was in better agreement with the fundamental crack growth rate curve when the crack closure only in the repetition of KL was taken into account, than when the closure at both stress levels of KH and KL were considered.

収録刊行物

  • 材料

    材料 36 (411), 1368-1374, 1987

    公益社団法人 日本材料学会

被引用文献 (1)*注記

もっと見る

キーワード

詳細情報 詳細情報について

問題の指摘

ページトップへ