Elastic constants of sintered alumina for X-ray stress measurement.

DOI Web Site 4 Citations

Bibliographic Information

Other Title
  • 焼結アルミナのＸ線的弾性定数
  • ショウケツ アルミナ ノ Xセンテキ ダンセイ テイスウ

Search this article

Abstract

The X-ray elastic constants of sintered polycrystalline alumina (with 99% purity) were measured for the diffraction planes (1. 0. 10) and (220) by using Cr-Kα radiation and for (146) and (4. 0. 10) by using Cu-Kα radiation, and the results were compared with the theoretical values obtained from the elastic constants of a single crystal on the bases of Reuss and Voigt models. The measured value of E/(1+ν) (E=Young's modulus, ν=Poisson's ratio) got smaller in the order of (146), (1. 0. 10), (220), (4. 0. 10). This order agreed with the theoretical prediction, although the value itself was smaller than the predicted value. Further comparsion of E and ν between the theory and the experiment indicates a necessity for making a suitable polycrystal model including the second phase or pores.

Journal

Citations (4)*help

See more

Keywords

Details 詳細情報について

Report a problem

Back to top