We have synthesized the pure single phase of aluminium tri-hydrogen bis (orthophosphate) monohydrate [AlH3(PO4)2·H2O] by using hydrophilic organic solvent, with high efficiency. It is a material with layered structure. The optimum condition to prepare it was as follows; the mixtures of 75wt% H3PO4 and Al(OH)3 (0.1mol) (molar ratio of H3PO4 to Al(OH)3=4.0) was refluxed at 94°C for 6 hours under stirring in 1-propanol (200cm3). Shape of products obtained was needle, and its length increased from 5μm to 80μm with increasing the reaction times. The maximal acid strength and amount of acid of solid surface were pKa=+1.5 and 1.81-2.13 (x10-2mmolg-1), respectively. AlH3(PO4)2·H2O changed to AlPO4 (berlinite, cristobalite-form) and Al(H2PO4)3 (B-form, C-form) by dehydration of monohydrate at 160°C.
収録刊行物
-
- 材料
-
材料 49 (6), 596-601, 2000
公益社団法人 日本材料学会
- Tweet
キーワード
詳細情報 詳細情報について
-
- CRID
- 1390282680369859200
-
- NII論文ID
- 110002294003
-
- NII書誌ID
- AN00096175
-
- ISSN
- 18807488
- 05145163
-
- NDL書誌ID
- 5377229
-
- 本文言語コード
- ja
-
- データソース種別
-
- JaLC
- NDL
- Crossref
- CiNii Articles
-
- 抄録ライセンスフラグ
- 使用不可