On the fatigue crack propagation behavior under repeated impacts using a new type of impact fatigue testing machine.

DOI Web Site Open Access

Bibliographic Information

Other Title
  • 衝撃疲労試験機の製作と衝撃荷重下でのステンレス鋼の疲労き裂成長速度挙動について
  • ショウゲキ ヒロウ シケンキ ノ セイサク ト ショウゲキ カジュウカ デ ノ

Search this article

Description

Machines and structures often encounter repeated impacts in practice. So, it is very important to study fatigue fracture of steel under repeated impacts. Usually a rotating disk type impact fatigue testing machine is used for such study, but the analysis of the data obtained by using this machine is considerably difficult, because the impact phenomenon is transient and has complex characters. So, a new type of machine was made by modifying a rotating disk type impact fatigue testing machine, and fatigue tests under repeated impacts were carried out. Then, the influences of velocity of repeated impacts and stress ratio on the fatigue crack growth rate of stainless steel were investigated by means of fracture mechanics and fractography. The difference in crack growth rate between repeated impacts and more gradually-applied cyclic load was large. This difference was explained by the effective stress intensity factor based on the equivalent stress ratio which includes the repeated impact loading effect.

Journal

Keywords

Details 詳細情報について

Report a problem

Back to top