- The Elevated Temperature and Thermal Shock Fracture Toughnesses of Nuclear Pressure Vessel Steel
- ゲンシロ アツリョク ヨウキ コウ ノ コウオン オヨビ ネツ ショウゲキ ハ
この論文をさがす
抄録
Thermal shock experiments were conducted on nuclear pressure vessel steel A533 Grade B Class 1. Elastic-plastic fracture toughness tests were carried out within the same high temperature range of the thermal shock experiment and the relation between stretched zone width, SZW and J-integral was clarified. An elastic-plastic thermal shock fracture toughness value, Jtsc was evaluated from a critical value of stretched zone width, SZWtsc at the initiation of thermal shock fracture by using the relation between SZW and J. The Jtsc value was compared with elastic-plastic fracture toughness values, JIc, and the deference between the Jtsc and JIc values was discussed.<br>The results obtained are summarized as follows;<br>(1) The relation between SZW and J before the initiation of stable crack growth in fracture toughness test at a high temperature can be expressed by the following equation regardless of test temperature, <br>SZW=95(J/E), <br>where E is Young's modulus.<br>(2) Elevated temperature fracture toughness values ranging from room temperature to 400°C are nearly constant regardless of test temperature. It is confirmed that upper shelf fracture toughness exists.<br>(3) Thermal shock fracture toughness is smaller than elevated temperature fracture toughness within the same high temperature range of thermal shock experiment.
収録刊行物
-
- 材料
-
材料 28 (308), 421-426, 1979
公益社団法人 日本材料学会
- Tweet
詳細情報 詳細情報について
-
- CRID
- 1390282680394043392
-
- NII論文ID
- 110002298121
-
- NII書誌ID
- AN00096175
-
- ISSN
- 18807488
- 05145163
-
- NDL書誌ID
- 2051704
-
- データソース種別
-
- JaLC
- NDL
- Crossref
- CiNii Articles
-
- 抄録ライセンスフラグ
- 使用不可