過大過小応力負荷条件下のき裂進展（平均応力波形の影響）

DOI Web Site

書誌事項

タイトル別名
  • Crack growth characteristics of a high strength steel under application of over- and understresses(Effect of the mean stress wave form).
  • カダイ カショウ オウリョク フカ ジョウケンカ ノ キレツ シンテン ヘイキ
  • Effect of the Mean Stress Wave Form
  • 平均応力波形の影響

この論文をさがす

抄録

Push-pull fatigue tests were conducted on 80kgf/mm2 steel under the combination of regularly applied understresses and intermittently applied overstresses. The mean stress superimposed on understresses changed periodically to form a overstress range pair at the time of the mean stress change. The effects of understress application, mean stress superposition on understresses and the mean stress wave form on the crack growth rate were investigated. Crack initiation and propagation lives in the tests conducted under the combination of over- and under-stresses were much shorter than expected when only the overstress cycles were counted, neglecting the damage of understresses. The stress amplitude even about 50% of the endurance limit of the steel was judged effective to make both of crack initiation and growth lives shorter. Crack initiation and growth lives in the tests with the sporadic down-spike stress change and with the rectangular stress change seemed almost equal to each other, and much shorter than those for the constant amplitude test. In two-step P-N interval tests, the crack growth rate was higher than that for the two-step N-P interval test, and even crack growth rate for the N-P test was higher than that for the completely reversed constant amplitude test at relatively smaller values of ΔK.

収録刊行物

  • 材料

    材料 38 (427), 404-409, 1989

    公益社団法人 日本材料学会

キーワード

詳細情報 詳細情報について

問題の指摘

ページトップへ