Nafion膜の構造と力学特性

  • 石田 拓也
    京都大学大学院工学研究科材料化学専攻
  • 葛西 裕
    青森県工業総合研究センター新エネルギー技術研究部
  • 浦山 健治
    京都大学大学院工学研究科材料化学専攻
  • 瀧川 敏算
    京都大学大学院工学研究科材料化学専攻

書誌事項

タイトル別名
  • Structure and Mechanical Properties of Nafion Membranes
  • Nafion マク ノ コウゾウ ト リキガク トクセイ

この論文をさがす

抄録

Thermal and mechanical properties of Nafion membranes in the dry and swollen states have been examined. The results of differential scanning calorimetry (DSC) and dynamic viscoelasticity measurements give the glass transition temperature (Tg) of the membranes lying around 120°C, which is close to that of polytetrafluoroethylenes (PTFEs ; Tg∼115°C). This shows that Tg of the Nafion membranes stems from the relaxation of PTFE main chains of the Nafion membranes. Stress-strain curves of the dry membranes below Tg exhibit the yielding that originates from the failure of the glassy matrix, i. e., the PTFE domains in the membranes. The Nafion membranes swollen by water also show the yielding of the stress-strain curves, i.e., no plasticization effect takes place in the PTFE domains. This suggests that water is localized in hydrophilic domains in the Nafion films. A finite water flow is observed in the water permeability measurement using the static pressures. These results clearly indicate a bicontinuous microphase separated structure composed of hydrophobic and hydrophilic domains.

収録刊行物

  • 材料

    材料 56 (11), 1005-1009, 2007

    公益社団法人 日本材料学会

参考文献 (5)*注記

もっと見る

詳細情報 詳細情報について

問題の指摘

ページトップへ